【摘要】：基于壓入法將玻璃纖維網(wǎng)布嵌入到聚乙烯(PE)復(fù)合塑料建筑模板內(nèi),并對其力學(xué)性能進(jìn)行研究。結(jié)果表明,靜曲強(qiáng)度及彈性模量隨著玻璃纖維網(wǎng)布尺寸增大而大幅降低,而剪切強(qiáng)度受玻璃纖維網(wǎng)布尺寸的影響較小,玻璃纖維網(wǎng)布的壓入深度不大于PE復(fù)合塑料建筑模板厚度的1/3。通過壓入玻璃纖維網(wǎng)布可大幅提升PE復(fù)合塑料建筑模板的力學(xué)性能。
[Abstract]:Glass fiber mesh was embedded into polyethylene (PE) composite plastic building template based on indentation method, and its mechanical properties were studied. The results show that the static flexural strength and elastic modulus decrease significantly with the increase of glass fiber mesh size, while the shear strength is less affected by glass fiber mesh size. The penetration depth of glass fiber mesh is not more than 1 / 3 of the thickness of PE composite plastic building formwork. The mechanical properties of PE composite plastic building formwork can be greatly improved by pressing fiberglass mesh cloth.
【作者單位】： 烏海職業(yè)技術(shù)學(xué)院建筑工程系;內(nèi)蒙古建筑職業(yè)技術(shù)學(xué)院裝飾與藝術(shù)設(shè)計學(xué)院;
【基金】：國家自然科學(xué)基金(50968010)
【分類號】：TB332;TQ325.12

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 ;可降解復(fù)合塑料及其制備方法[J];石油化工;2008年09期

2 ;浙江開發(fā)全天然可降解竹基生物復(fù)合塑料[J];塑料科技;2012年09期

3 ;超高分子復(fù)合塑料產(chǎn)品通過鑒定[J];塑料工業(yè);2002年04期

4 ;超高分子復(fù)合塑料[J];技術(shù)與市場;2002年05期

5 戴欣;尚慶坤;李詩春;修艷華;馮雪嬌;傅高峰;閆蕊;;納米-CaCO_3/OMMT/HDPE三元復(fù)合塑料的制備和性能[J];應(yīng)用化學(xué);2008年11期

6 計其達(dá);增強(qiáng)復(fù)合塑料與木材[J];工程塑料應(yīng)用;1981年01期

7 辛化丹;熱塑性復(fù)合塑料材料的設(shè)計和應(yīng)用(連載之六)[J];塑料科技;1983年03期

8 C.C.查密斯;陳紹棣;;增強(qiáng)復(fù)合塑料的微應(yīng)力預(yù)測[J];國外塑料;1989年04期

9 李德銀;扁絲級增強(qiáng)復(fù)合塑料[J];塑料通訊;1995年01期

10 徐佩弦;復(fù)合塑料的熔合縫[J];工程塑料應(yīng)用;1998年08期

相關(guān)重要報紙文章 前2條

1 ;可生物降解的復(fù)合塑料[N];經(jīng)濟(jì)參考報;2002年

2 記者 廉士傳;吉林省東承住化汽車復(fù)合塑料項目投產(chǎn)[N];四平日報;2012年

相關(guān)碩士學(xué)位論文 前1條

1 袁靜蘭;碳纖維增強(qiáng)導(dǎo)電復(fù)合塑料的非接觸式電磁感應(yīng)加熱研究[D];北京化工大學(xué);2016年

，

本文編號：2166709