【摘要】：以硅氧烷為疏水劑,采用浸漬法在具有開放及封閉微結(jié)構(gòu)的金屬鋁板上制備了超疏水表面,系統(tǒng)考查了表面微結(jié)構(gòu)設(shè)計對材料疏水及防冰性能的影響。結(jié)果表明,超疏水表面靜態(tài)接觸角隨結(jié)除冰次數(shù)的增加而減少,滾動角隨結(jié)除冰次數(shù)的增加而增大,且在多個結(jié)冰除冰循環(huán)后,表面開放微結(jié)構(gòu)的金屬鋁板喪失其超疏水性,表面封閉微結(jié)構(gòu)的金屬鋁板仍保持其超疏水性。進一步實驗研究表明,在多個結(jié)冰除冰循環(huán)后,在相同結(jié)冰條件下,水滴在表面為開放微結(jié)構(gòu)的金屬鋁板上的結(jié)冰時間遠長于表面為封閉結(jié)構(gòu)的金屬鋁板。
[Abstract]:Using siloxane as hydrophobic agent, the superhydrophobic surface of aluminum plate with open and closed microstructures was prepared by impregnation method. The effects of surface microstructure design on hydrophobic and anti-ice properties of the materials were systematically investigated. The results show that the static contact angle of superhydrophobic surface decreases with the increase of deicing times, and the rolling angle increases with the increase of deicing times. The surface closed microstructure of the metal aluminum plate still keeps its hydrophobicity. Further experimental studies show that under the same icing conditions, the freezing time of water droplets on metal aluminum plates with open microstructures is much longer than that on metal aluminum plates with closed surface structure after several deicing cycles.
【作者單位】： 中國民用航空總局第二研究所;四川師范大學化學與材料科學學院;
【基金】：國家自然基金項目(U153310152)
【分類號】：TB306

【相似文獻】

相關(guān)期刊論文 前3條

1 高海平;藺存國;張桂玲;王利;;表面微結(jié)構(gòu)防污研究[J];涂料工業(yè);2010年01期

2 徐鍵,夏海平,張約品,章踐立,王金浩;用光刻、軟刻和氧化硅球晶體模板制備表面微結(jié)構(gòu)[J];無機材料學報;2005年01期

3 許莉麗;李曉光;倪星元;沈軍;;微結(jié)構(gòu)與表面修飾對二氧化硅多孔薄膜疏水性能的影響[J];無機化學學報;2013年03期

相關(guān)會議論文 前1條

1 靳釗;余浩杰;;表面微結(jié)構(gòu)防污薄膜的研究初探[A];2011年全國高分子學術(shù)論文報告會論文摘要集[C];2011年

相關(guān)博士學位論文 前1條

1 呂通;基于形狀記憶環(huán)氧樹脂超疏水表面構(gòu)筑及其潤濕性調(diào)控[D];哈爾濱工業(yè)大學;2016年

相關(guān)碩士學位論文 前1條

1 羅劉闖;PBS/fGO復合材料及PBS基疏水材料的制備與性能[D];鄭州大學;2017年

，

本文編號：2182000